Preparation of the macroporous polysaccharide hemostatic complex materials and study on its performance in vitro |
XU Ling1 MA Xiaochun1 ZENG Lijun2 CHEN Miaoyuan2 WANG Yun2 JU Xuecheng1 QIU Ximei1 |
1.Peking University Shenzhen Institute, Guangdong Province, Shenzhen 518057, China;
2.Xiamen Gelfeel Biological Technology Co., Ltd., Fujian Province, Xiamen 361026, China |
|
|
Abstract Objective To evaluate the hemostatic effect of the macroporous polysaccharide hemostasis complex materials preliminarily, and to investigate the performance of the materials in vitro. Methods The hemostatic materials were prepared by γ-irradiation crosslinked method, and its structure, degradation in vitro and clotting performance were characterized by infrared spectrum and physicochemical test. Results The results showed that the crosslinked carboxymethylated-chitosan molecules had been made after the materials were irradiated, and its water absorption was of 3456%. The biodegradable degradation of the materials in lysozyme solution was 68% after 3 days and the degradation completed within 20 days. The clotting time was (25.33±2.45) s, which indicated the material adhered more red blood cells and platelets and showed the stronger blood clots. Conclusion The macroporous polysaccharide hemostasis complex materials prepared by γ-irradiation crosslinked method possess great solution absorption performance and blood coagulation performance, which has good application prospect in wound hemostasis.
|
|
|
|
|
[1] Sondeen JL,Pusateri AE,Coppes VG,et al. Comparison of 10 different hemostatic dressings in an aortic injury [J]. J Trauma,2003,54(2):280-285.
[2] 童正阳.可吸收生物止血材料研究进展[J].世界最新医学信息文摘,2017,17(2):43.
[3] 王亚会,赵家义,刘轶清,等.战创伤急救止血技术的研究进展[J].第二军医大学学报,2017,38(5):652-658.
[4] Zeltser R,Krejci-Papa N. Surgical pearl:localized pressure from routine surgical instruments provides safe and effective temporary hemostasis [J]. J Am Acad Dermatol,2005, 53(3):496-497.
[5] Busilacchi A,Gigante A,Mattioli-Belmonte M,et al. Chitosan stabilizes platelet growth factors and modulates stem cell differentiation toward tissue regeneration [J]. Carbohyd Polym,2013,98(1):665-676.
[6] 王婧奇.多糖/沸石复合止血材料的研制[D].上海:东华大学,2015.
[7] 陈晓龙.淀粉基止血材料的制备及其性能研究[D].上海:华东理工大学,2013.
[8] 王春,谷天祥,喻磊,等.再生氧化纤维素在严重骨质疏松体外循环手术胸骨止血中的作用[J].中国组织工程研究与临床康复,2011,15(25):4739-4742.
[9] 邓乐君,樊鸿浩,李伟达,等.可吸收性止血材料的生物相容性研究进展[J].中国生物医学工程学报,2016,35(2):241-246.
[10] 张自强,张以河,祖耀先,等.胶原蛋白海绵对肝脏创伤止血的效果[J].中国组织工程研究,2017,21(30):4873-4878.
[11] 虞昆,孙可望.胶原蛋白海绵对腔镜甲状腺手术止血效果的研究[J].外科理论与实践,2016,21(3):267-268.
[12] 杨照.高分子羧甲基壳聚糖的性质及其止血和愈创功能研究[D].青岛:中国海洋大学,2012.
[13] 黄玉芬,邹励宏,高洁,等.烷基化壳聚糖的制备及止血效果[J].中国组织工程研究,2016,20(52):7878-7884.
[14] 侯春林,顾其胜.几丁质与医学[M].上海:上海科学技术出版社,2001:165-167.
[15] Chen XG,Park HJ. Chemical characteristics of O-carboxymethyl chitosans related to the preparation conditions [J]. Carbohyd Polym,2003,53(4):355-359.
[16] 李冬冬,吴岳林,华万森,等.羧甲基壳聚糖络合碘材料的止血活性评价[J].药学实践杂志,2015,33(2):125-126.
[17] 钟庆坤,欧阳茜茜,李思东,等.壳聚糖止血材料及应用的研究进展[J].轻工科技,2017,33(6):49-51,57.
[18] Yan EY,Hao XY,Cao LL,et al. Preparation and characterization of carboxymethyl chitosan hydrogel [J]. Pigm Resin Technol,2016,45(4):246-251.
[19] 刘霞,赵桂芝,王昱霁,等.羧化壳聚糖止血及其生物安全性评价[J].中国组织工程研究,2017,21(22):3561-3566.
[20] Barba BJD,Tranquilan-Aranilla C,Abad LV. Hemostatic potential of natural/synthetic polymer based hydrogels crosslinked by gamma radiation [J]. Radiat Phys Chem,2016,118:111-113. |
|
|
|